热处理工艺对硬质合金表面金刚石薄膜 附着性能的影响
热处理工艺对硬质合金表面金刚石薄膜 附着性能的影响
作者:
作者单位:

作者简介:

通讯作者:

基金项目:

国家自然科学基金项目( 5 1 4 0 2 3 4 4 ) ; 广东省创新团队项目( 2 0 1 3 C 0 9 0 ) ; 深圳市技术创新计划技术攻关项目 (JSGG20160301173854530);深圳市海外高层次人才创新创业计划(KQJSCX20160301145319);深圳市基础研究项目(JCYJ20160122143847150)

伦理声明:



Effects of Heat-Treatment on the Adhesive Strength of Diamond Films Coated on the Cemented Carbide Substrates
Author:
Ethical statement:

Affiliation:

Funding:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    文章针对提高硬质合金刀具金刚石涂层结合力问题,提出了一种热处理和酸处理相结合的预处 理工艺,详细研究和分析了 800~1 000℃ 范围内,热处理温度变化与硬质合金刀具表面形貌、金刚石涂 层质量、涂层与刀具间附着力之间的关系。热处理工艺显著降低了生长过程中钴对金刚石涂层石墨化的 催化作用,进一步提高了碳化钨颗粒的比表面积及金刚石二次形核密度,得到的金刚石涂层晶粒尺寸及 压应力较小。过高的热处理温度虽然可以细化基体表面,增加基体与金刚石涂层之间的“机械锁合”作 用,但预处理过程中残留在基体表面的深坑却不利于金刚石涂层附着力的提高,在外力的作用下容易在 深坑附近产生微裂纹。实验结果显示,在氩气气氛中,900℃ 时热处理的硬质合金基体表面生长的金刚 石涂层质量和附着力最佳。

    Abstract:

    In this paper, to improve the adhesive strength of diamond films for the cemented substrates before depositing process, a new approach combined with heat-treatments and acid treatments was investigated. Relations between heat-treatments and surface morphologies, quality of diamond films and the adhesive strength were analyzed within the temperature range of 800~1 000℃. Heat treatment on the cemented substrate was an effective method to improve the adhesive strength for diamond films. With the heating process, large tungsten particles can be refined to small size which can enhance the “interlock functions” between diamond films and the substrate, and improve the density of secondary nucleation. The redundant metal cobalt was removed effectivelyto prevent the catalytic actions, which may cause the transformation from diamond to graphite. However, the adhesive strength was decreased with high temperature heating process subject to the holes left on the substrate surface. Results show that the samples heated at 900℃ owned the strongest adhesive strength and least compressive stress for diamond films.

    参考文献
    相似文献
    引证文献
引用本文

引文格式
谷继腾,杨 扬,唐永炳.热处理工艺对硬质合金表面金刚石薄膜 附着性能的影响 [J].集成技术,2017,6(4):80-88

Citing format
GU Jiteng, YANG Yang, TANG Yongbing. Effects of Heat-Treatment on the Adhesive Strength of Diamond Films Coated on the Cemented Carbide Substrates[J]. Journal of Integration Technology,2017,6(4):80-88

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
历史
  • 收稿日期:2017-05-04
  • 最后修改日期:2017-05-27
  • 录用日期:
  • 在线发布日期: 2017-07-19
  • 出版日期: