肿瘤热化疗用磁性聚合物微球的制备及表征
作者:
作者单位:

作者简介:

通讯作者:

基金项目:

国家自然科学基金项目(31500773);深圳市基础研究自由探索项目(JCYJ20150401150223643)

伦理声明:



Preparation and Characterization of Magnetic Polymer Microspheres for Tumor Magnetic Hyperthermia
Author:
Ethical statement:

Affiliation:

Funding:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
    摘要:

    以磁性四氧化三铁(Fe3O4)纳米粒子和可降解聚合物聚乳酸-羟基乙酸共聚物为原料,采用乳 化-溶剂挥发法制备获得磁性聚合物微球。通过傅里叶红外光谱、热失重曲线、透射电子显微镜、振 动样品磁强计对所制备的磁性聚合物微球的各项性能进行表征,并利用高频磁感应设备测定磁性聚合 物微球的磁感应加热性能。结果表明,所制备的两种磁性聚合物微球中 Fe3O4 纳米粒子的含量分别为 10.1% 和 18.8%,其比饱和磁化强度分别为 2.3 emu/g 和 6.8 emu/g;在高频磁场作用下,8 min 内升温 分别可达到 9℃ 和 16.5℃,完全满足肿瘤磁热疗的升温需求,在肿瘤磁热疗及热化疗结合治疗中有着 很好的应用潜力。

    Abstract:

    In this paper, magnetic polymer microspheres were prepared via emulsion-solvent evaporation method, with magnetic Fe3O4 nanoparticles and biodegradable polymer poly(lactic-co-glycolic acid). The structures and properties of microspheres were characterized with Fourier transform infrared spectroscopy, thermogravimetric analysis, transmission electron microscopy and vibrating sample magnetometer, and the electromagnetic induction heating property was also investigated. The obtained two magnetic polymer microspheres with Fe3O4 content of 10.1% and 18.8% exhibited saturation magnetization values of 2.3 emu/g and 6.8 emu/g, and temperature increased 9℃ and 16.5℃ under the electromagnetic induction. Results suggest that the obtained magnetic polymer microspheres meet the heating requirement of hyperthermia and have potential applications in magnetic hyperthermia or thermochemotherapy of cancer.

    参考文献
    相似文献
    引证文献
引用本文

引文格式
李鹏辉,江 敏,李炜澔,等.肿瘤热化疗用磁性聚合物微球的制备及表征 [J].集成技术,2017,6(5):1-7

Citing format
LI Penghui, JIANG Min, LI Weihao, et al. Preparation and Characterization of Magnetic Polymer Microspheres for Tumor Magnetic Hyperthermia[J]. Journal of Integration Technology,2017,6(5):1-7

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
历史
  • 收稿日期:2017-08-12
  • 最后修改日期:2017-08-24
  • 录用日期:
  • 在线发布日期: 2017-09-20
  • 出版日期: